TC6 qotishmasi - bu yaxshi keng qamrovli ishlashga ega bo'lgan + ikki fazali issiq kuchli titanium qotishmasining martensitik Ti-Al-Mo-Cr-Fe-Si tizimi, nominal tarkibi Ti-6Al-2.5Mo -1.5Cr-0.5Fe-0.3Si va / oʻtish harorati 960 va 1000 daraja orasida. Oddiy titanium qotishmasining yuqori o'ziga xos kuch va yaxshi korroziyaga chidamliligi kabi afzalliklariga qo'shimcha ravishda, qotishma xona haroratida va yuqori haroratda yaxshi keng qamrovli mexanik xususiyatlarga ega va xizmat ko'rsatish harorati 450 darajaga yetishi mumkin. U ko'pincha aero-dvigatel pichoqlari, turbinali disklar va boshqa muhim qismlarni ishlab chiqarishda qo'llaniladi, shuningdek, samolyot spacer ramkalari, bo'g'inlari va boshqa qismlarni ishlab chiqarishda ham qo'llanilishi mumkin. Xitoyda TC6 titanium qotishma zarblari, to'qimalari, quvurlari va barlari va boshqalarni qayta ishlash texnologiyasi va ish faoliyatini optimallashtirish bo'yicha juda ko'p ishlar amalga oshirildi, TC6 qotishma plitalari bo'yicha kamroq tadqiqotlar olib borildi. Tadqiqotchilar TC6 plitalarini sovuq haddeleme jarayonini nazorat qilish orqali TC6 plitalarini sovuq haddeleme bilan ishlov berishning asosiy jarayon parametrlarini aniqladilar va TC6 plitalarining sovuq haddeleme ishlash ko'rsatkichlarini o'rgandilar.
Eksperimental TC6 titanium qotishmasi ingot vakuumli o'z-o'zidan iste'mol qilinadigan elektr kamon pechida uch marta eritish orqali olinadi va uning o'tish harorati 975-985 daraja va o'ziga xos kimyoviy tarkibi (og'irlik%): Al6.2, Mo2.5, Cr1.4, Fe{{10}}.41, Si0.29, O0.10, Zr<0.01, C<0.01, N<0.01, and Ti remainder. The experimental TC6 ingots were opened in the β-phase region and forged into slabs in the α+β two-phase region. Slabs were hot rolled above the β-transition temperature to open billets, rolled to 3.5 mm in the α+β two-phase zone, and then cold rolled for work-hardening experiments after intermediate annealing and pickling. Processing rate of every 5% increase, from the head of the plate cut 200mm long piece of experimental material, the remaining plates continue to roll, so repeatedly rolled, sampling, until the plate appears edge cracks or surface cracks. Then the cut 200mm experimental material with different processing deformation was tested, and the thickness, width, edge crack, organization and mechanical properties of the experimental plates were tested respectively.
Yuqoridagi eksperimental mikro tuzilma Axiovert 200 MAT optik mikroskopida kuzatildi va mexanik xususiyatlar Instron 5885 valentlik sinov mashinasida sinovdan o'tkazildi. Sinov natijalari quyidagicha:
(1) Sovuq haddeleme ishining qattiqlashuv egri chizig'idan shuni ko'rish mumkinki, ishlov berish tezligi oshishi bilan valentlik kuchi va oqish kuchi ortadi, cho'zilish asta-sekin pasayadi, bu asosan dislokatsiya zichligi oshishi bilan bog'liq. sovuq prokatni qayta ishlash tezligi va ishning qattiqlashuvining kuchayishi. Qayta ishlash tezligi taxminan 27% ga yetganda, tortishish kuchi va oquvchanlik egri chizig'i tekislanishga intiladi, bu uning qiyin deformatsiya bosqichiga o'tishini ko'rsatadi.
(2) TC6 titanium qotishma plitasi Z katta sovuq haddeleme ishlov berish tezligi 30,3% ga yetishi mumkin, bu vaqtda materialning cho'zilishi 5,8% ga tushadi, plastinka yuzasida ajinlar va konvekslik, chekka yoriqlar paydo bo'la boshlaganini kuzating. Yoyilgan kengligi 20 mm bo'lsa, sovuq prokatni qayta ishlash darajasi 30,3% ni tashkil qiladi.